- The%20CLT%20increased%20the%20HRR%20of%20the%20wood%20crib. obtainsSupportFrom ZIYHH3 assertion.
- The%20fire%20spread%20rate%20before%20the%20ignition%20of%20the%20ceiling%20was%2054%20mm%2Fmin%20%280.9%20mm%2Fs%29. obtainsSupportFrom ZIYHH3 assertion.
- The%20fire%20spread%20rate%20after%20the%20ignition%20of%20the%20ceiling%20was%201.2%20m%2Fmin%20%2820%20mm%2Fs%29. obtainsSupportFrom ZIYHH3 assertion.
- The%20char%20depth%20was%20strongly%20non-uniform%20across%20the%20ceiling. obtainsSupportFrom ZIYHH3 assertion.
- The%20largest%20char%20depth%20along%20the%20X-axis%20was%20located%20where%20the%20highest%20temperatures%20were%20measured. obtainsSupportFrom ZIYHH3 assertion.
- The%20arithmetic%20average%20of%20the%20char%20depth%20of%20the%20entire%20CLT%20ceiling%20was%2026%20mm. obtainsSupportFrom ZIYHH3 assertion.
- Delamination%20occurred%20in%20the%20centre%20of%20the%20compartment%20where%20the%20char%20depth%20was%20thicker. obtainsSupportFrom ZIYHH3 assertion.
- Even%20for%20the%20areas%20with%20delamination%2C%20the%20charring%20had%20not%20reached%20the%20glue-line. obtainsSupportFrom ZIYHH3 assertion.
- The%20maximum%20temperature%20at%2040%20mm%20depth%20was%20164%E2%80%93194%C2%B0C%20around%20120%20min. obtainsSupportFrom ZIYHH3 assertion.
- The%20temperature%20below%20the%20ceiling%20at%20120%20min%20was%20approximately%20220%C2%B0C%20and%20declining. obtainsSupportFrom ZIYHH3 assertion.
- From%20the%20point%20when%20the%20ceiling%20was%20ignited%2C%20the%20fire%20dynamics%20changed%20completely%2C%20and%20the%20flames%20spread%20quickly%20across%20the%20ceiling%20and%20wood%20crib. obtainsSupportFrom ZIYHH3 assertion.
- The%20fire%20travelled%20back%20and%20forth%20in%20four%20distinct%20flashing%20waves%20within%2013%20min. obtainsSupportFrom ZIYHH3 assertion.
- After%20a%20short%20post-flashover%20phase%2C%20the%20intensity%20of%20the%20fire%20was%20rapidly%20reduced%2C%20and%20the%20CLT%20ceiling%20self-extinguished%20over%20a%20period%20of%20approx.%2010%20min. obtainsSupportFrom ZIYHH3 assertion.
- The%20charring%20was%20most%20pronounced%20in%20the%20centre%20of%20the%20ceiling%20and%20towards%20the%20back%20of%20the%20room. obtainsSupportFrom ZIYHH3 assertion.
- Some%20delamination%20was%20observed%2C%20although%20the%20average%20char%20depth%20did%20not%20reach%20the%20glue%20line. obtainsSupportFrom ZIYHH3 assertion.
- No%20reignition%20or%20fire%20growth%20was%20observed%20within%204%20h%20after%20self-extinguishment. obtainsSupportFrom ZIYHH3 assertion.
- External%20flames%20were%20present%20during%20the%20flashing%20waves%20and%20for%20a%20short%20period%20after%20flashover. obtainsSupportFrom ZIYHH3 assertion.
- The%20incident%20heat%20flux%20at%20the%20fa%C3%A7ade%20was%20lower%20than%20the%20highest%20values%20measured%20in%20other%20comparable%20CLT%20compartment%20experiments. obtainsSupportFrom ZIYHH3 assertion.
- The%20fire%20appeared%20neither%20as%20a%20true%20fuel-controlled%20fire%20nor%20a%20ventilation-controlled%20fire%2C%20as%20it%20had%20elements%20of%20both. obtainsSupportFrom ZIYHH3 assertion.